阻燃耐候ABS FR25UHF 抗紫外线ABS
FR25UHF黄卡资料PDF下载
| Component - Plastics | E121562 |
|
| SABIC INNOVATIVE PLASTICS US L L C |
| AMERICAS - RESIN, 1 PLASTICS AVE, PITTSFIELD MA 01201-3662 |
| FR25UHF |
| Acrylonitrile Butadiene Styrene (ABS), "Cycolac", furnished as pellets |
| Min Thk | Flame |
|
| RTI | RTI | RTI |
| Color | (mm) | Class | HWI | HAI | Elec | Imp | Str |
| NC, BK | 1.6 | V-1 | 3 | 2 | 60 | 60 | 60 |
| 2.0 | V-1 | 3 | 2 | 60 | 60 | 60 |
| 2.5 | V-0 | 3 | 1 | 60 | 60 | 60 |
| 6.0 | V-0 | - | - | 60 | 60 | 60 |
| Comparative Tracking Index (CTI): | - | Inclined Plane Tracking (IPT): | - |
| Dielectric Strength (kV/mm): | 26 | Volume Resistivity (10x ohm-cm): | 15 |
| High-Voltage Arc Tracking Rate (HVTR): | - | High Volt, Low Current Arc Resis (D495): | - |
| Dimensional Stability (%): | - |
|
|
| ANSI/UL 94 small-scale test data does not pertain to building materials, furnishings and related contents. ANSI/UL 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components and parts of end-product devices and appliances, where the acceptability of the combination is determined by UL. |
Report Date: 1972-04-14
Last Revised: 2012-05-31 |
|
|
| IEC and ISO Test Methods |
| Test Name | Test Method | Units | Thk (mm) | Value |
| Flammability | IEC 60695-11-10 | Class (color) | 1.6 | V-1 (NC, BK) |
|
|
| 2.0 | V-1 (NC, BK) |
|
|
| 2.5 | V-0 (NC, BK) |
|
|
| 6.0 | V-0 (NC, BK) |
| Glow-Wire Flammability (GWFI) | IEC 60695-2-12 | C | 2.0 | 960 |
| Glow-Wire Ignition (GWIT) | IEC 60695-2-13 | C | 2.0 | 675 |
| IEC Comparative Tracking Index | IEC 60112 | Volts (Max) | 3.0 | CTI175 |
| IEC Ball Pressure | IEC 60695-10-2 | C | 3.0 | 75 |
| ISO Heat Deflection (1.80 MPa) | ISO 75-2 | C | - | - |
| ISO Tensile Strength | ISO 527-2 | MPa | - | - |
| ISO Flexural Strength | ISO 178 | MPa | - | - |
| ISO Tensile Impact | ISO 8256 | kJ/m2 | - | - |
| ISO Izod Impact | ISO 180 | kJ/m2 | - | - |
| ISO Charpy Impact | ISO 179-2 | kJ/m2 |
|
|
阻燃 防火ABS FR23 注塑
| 熔体流动速率 |
| 230℃/3.8kg | ASTM-D1238 | 4.0 | g/10min |
| 比重 |
|
| ASTM-D792 | 1.22 | g/cm3 |
| 模具收缩率 |
|
| ASTM-D955 | 0.5-0.9 | % |
| 拉伸强度 |
|
| ASTM-D638 | 41.4 | MPa |
| 弯曲模量 |
|
| ASTM-D790 | 2280 | MPa |
|
|
| ASTM-D790 | 66.9 | MPa |
| IZOD缺口冲击强度 |
| 23℃,3.18mm | ASTM-D256 | 133 | J/m |
| 热变形温度 |
| 1.80Mpa Unannealed,6.35mm | ASTM-D648 | 82.2 | ℃ |
| 阻燃等级 |
| 1.50mm,ALL | UL94 | V-0 |
|
"本公司是一家Sabic【即沙特基础公司SABIC Innovative Plastics】工程塑料专业代理。经营产品有Noryl(PPO改性聚苯醚）、Lexan（PC聚碳酸酯）、Ultem(PEI聚醚酰亚胺)、Valox(PBT聚丁烯对苯二甲酸酯)Cycoloy(PC与ABS合金）、Xenoy(PC/PBT合金）、Xylex(PC/PET合金），同时为广阻燃 防火ABS FR23 注塑
| 模具温度(Standard Molding) | 固定轴 | °C | 60 |
| 移动轴 | 80 |
| 低粘，流动性高PC TLL40CP 高流动PC |
|
|
|
|
| Hot Runner温度 | Manifold | °C | 260 |
| Valve nozzle | 260 |
| Nozzle温度 |
| °C | 260~240 |
| Cylinder温度 | 前端 | °C | 260 ~ 240 |
| 中部 | 250 ~ 230 |
| 下部 | 240 ~ 230 |
| 注塑压力 |
| kgf/cm2 | 600 |
| 干燥条件 | 干燥方式 | 干燥温度 | °C | 110 |
| 干燥时间 | hr | 2 ~ 4 |
| 热风方式 | 干燥温度 | °C | 110 |
| 干燥时间 | hr | 4 ~ 6 |
| 干燥后合适水分量 |
| % | < 0.02 |
| 计量速度 |
| rpm | 50 |
| rpm | 150 |
...