丙烯腈丁二烯苯乙烯
SABIC Innovative Plastics
产品说明
SABIC INP108 is a high rubber ABS impact modifier resin, and is based on polybutadiene rubber. Offers superior impact efficiency, especially at low temperatures. Reduces notch sensitivity when alloyed with engineering polymers. Disperses easily. Provides abrasion and chemical resistance to polymers.
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 添加剂 |
|
| 表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度 | IEC 60243-1 | ||
0.800 mm, 在油中 | 35 | kV/mm | |
1.60 mm, 在油中 | 26 | kV/mm | |
3.20 mm, 在油中 | 18 | kV/mm | |
| 相对电容率 | IEC 60250 | ||
50 Hz | 2.70 | ||
60 Hz | 2.70 | ||
1 MHz | 2.60 | ||
| 耗散因数 | IEC 60250 | ||
50 Hz | 4.0E-3 | ||
60 Hz | 4.0E-3 | ||
1 MHz | 9.0E-3 | ||
| 漏电起痕指数 | 600 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| UL 阻燃等级(1.50 mm, Testing by SABIC) | HB | UL 94 | |
| 灼热丝易燃指数(1.00 mm) | 650 | °C | IEC 60695-2-12 |
耐低温冲击ABS INP362 ABS
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 比重 | |||
-- | 0.998 | g/cm3 | ASTM D792 |
-- 1 | 1.01 | g/cm3 | ISO 1183 |
| 表观密度 | 0.35 | g/cm3 | ASTM D1895 |
| Mean Particle Size | 400.0 | μm | 内部方法 |
| Rubber Content | 32 | % | 内部方法 |
| Total NA Volatiles | 0.10 | % | 内部方法 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 肖氏硬度(邵氏 D) | 58 | ISO 868 |
| 注射 | 额定值 | 单位制 | |
|---|---|---|---|
| 干燥温度 | 85.0 到 95.0 | °C | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的*水分含量 | 0.10 | % | |
| 料斗温度 | 60.0 到 80.0 | °C | |
| 料筒后部温度 | 200 到 240 | °C | |
| 料筒中部温度 | 220 到 260 | °C | |
| 料筒前部温度 | 220 到 260 | °C | |
| 射嘴温度 | 210 到 250 | °C | |
| 加工（熔体）温度 | 220 到 260 | °C | |
| 模具温度 | 40.0 到 80.0 | °C |